Therefore , the nonionic surfactant can effectively intensify the seeded precipitation process of sodium aluminate solution.

非離子型表面活性劑能有效強(qiáng)化鋁酸鈉溶液晶種分解過程.

The preparation technique for cobaltous aluminate, the coating mold wall and casting process are also introduced.

介紹鋁酸鈷的制備 、 面層涂料的配制以及合金的澆注工藝.

Dawsonite decomposition method , a new process for producing sodium aluminate, is proposed.

提出了由絲鈉鋁石分解法制固體鋁酸鈉的新工藝.

Modified aluminum hydroxid was prepared by sodium aluminate in Rotating Packed Bed ( RPB ) coupled with hydrolysis.

利用旋轉(zhuǎn)填充床碳分-水熱耦合法制備改性氫 氧化鋁.

Strontium aluminate long persistence phosphors were prepared through homogeneous precipitation method.

采用均勻沉淀法制備鋁酸鍶基質(zhì)長余輝發(fā)光材料.

Decomposition mechanism of the sodium aluminate solution were introduced in the article, the strengthen.

本文同時(shí)也綜述了鋁酸鈉溶液種分分解機(jī)理及其強(qiáng)化手段.

Hydrometallurgical removal of sulphur from industral sodium aluminate solution with barium aluminate is studied.

介紹了用鋁酸鋇從工業(yè)鋁酸鈉溶液中濕法除硫的試驗(yàn)結(jié)果.

The effect of sulpho aluminate cement on the performance of Portland cement was studied.

研究了硫鋁酸鹽水泥熟料對復(fù)合硅酸鹽水泥性能的影響.

The dry shrinkage of Portland cement and calcium aluminate cement composite cement system trends towards enlarger.

復(fù)合體系的脹后干縮有增大的趨勢.

The aluminate phosphor BaMgAl 10 O 17∶ Eu 2 + ( BAM ) was successfully synthesized by rapid combustion process at 600 ℃ furnace temperature.

應(yīng)用燃燒法在較低溫度(600℃)下,于空氣中快速合成BaMgAl10O17∶Eu2+ ( BAM ) 熒光體.